SCHULAMID® 612 GF 50 H
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hA8Fzc_SCHULAMID-612-GF-50-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% glass fiber reinforced Polyamid 612 compound, heat stabilised |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.54 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16500 | 12000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 200 | 145 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | 2.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1(23°C) | 15000 | -- | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 300 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength (23°C) | 2.5 | -- | % | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | -- | kJ/m² | |
| 23°C | 13 | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 64 | -- | kJ/m² | |
| 23°C | 70 | 72 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 218 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 216 | -- | °C | ISO 306/A50 |
| -- | 208 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | 50 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 725 | -- | °C | |
| 3.00 mm | 800 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 750 | -- | °C | |
| 3.00 mm | 825 | -- | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PA6 B401 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| NuSil MED3-4013 | NuSil Technology | Silicone | NuSil |
| Generic Nylon 612 - Glass Bead | Generic | Nylon 612 | Generic |
| Mafill® CR HC 5941 | Ravago Group | PP Homopolymer | Mafill® |
| LNP™ LUBRICOMP™ ML004LS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ LUBRICOMP™ |