Vyncolit® G900
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hA3Vgl_VyncolitG900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® G900 is a glass fiber reinforced resol resin based molding material. It has good mechanical properties, combined with superior electrical insulation properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.80 | g/cm³ | ISO 1183 |
| Apparent Density | 0.79 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.23 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.11 | % | ISO 62 |
| Post Shrinkage | 0.070 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.3 | % | ISO 178 |
| Tensile Modulus | 18000 | MPa | ISO 527-2 |
| Tensile Stress | 114 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.88 | % | ISO 527-2 |
| Flexural Modulus | 16000 | MPa | ISO 178 |
| Flexural Stress | 185 | MPa | ISO 178 |
| Compressive Stress | 257 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.4 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 13 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 151 | °C | ISO 75-2/Af |
| 8.0 MPa, not annealed | 136 | °C | ISO 75-2/Cf |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 5.0E-6 | cm/cm/°C | TMA |
| Lateral | 4.0E-5 | cm/cm/°C | TMA |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 7.4E+13 | ohms | IEC 60093 |
| Volume Resistivity | 3.8E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 32 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POULOY 2001 | POLYROCKS CHEMICAL CO., LTD | PC+ABS | POULOY |
| Sanren F200 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Tenogel® ABS A3 G20 NTLA010 AB321 | Petropol Industry and Trade of Polymers LTDA | ABS | Tenogel® ABS |
| TRILOY® 190 | Samyang Corporation | PC+PBT | TRILOY® |
| ENFLEX S4025A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |