| DESCRIPTION: Epocast® 1626-A/B epoxy syntactic is a two-part compound designed for core filling, edge sealing, and bushing and fastener potting of honeycomb structures. The easy-to-handle viscous paste has low flow characteristics. Epocast® 1626-A/B epoxy syntactic is a toughened system which resists cracking and is especially well suited for applications that may involve exposure to high vibration and wide temperature cycling. Epocast® 1626-A/B epoxy syntactic has good retention of strength after environmental aging and is qualified to BMS 5-28, Type 26. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D1622 | ||
| -- 1 | 0.500 | g/cm³ | ASTM D1622 |
| -- 2 | 0.650 | g/cm³ | ASTM D1622 |
| -- 3 | 1.10 | g/cm³ | ASTM D1622 |
| Viscosity | ASTM D2196 | ||
| 25°C 4 | Paste | ASTM D2196 | |
| 25°C 5 | Paste | ASTM D2196 | |
| 25°C 6 | Paste | ASTM D2196 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time - 50 gms (25°C) 7 | 1.0 | hr | ASTM D2471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Lap Shear - AL/AL (25°C) | 4.83 | MPa | ASTM D1002 |
| T-Peel - AL/AL | 16.0 | kN/m | ASTM D1876 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 48 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 4.14 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 28 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 29 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE: 7 days at 77°F (25°C) or 24 hours at 77°F (25°C), plus 2 hours at 160°F (71°C). |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | System |
| 3 . | Hardener |
| 4 . | System |
| 5 . | Hardener |
| 6 . | Resin |
| 7 . | System |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® H080MA | Reliance Industries Limited | PP Homopolymer | REPOL® |
| TRIMMA® SD6310H | Samyang Corporation | Acrylic (PMMA) | TRIMMA® |
| Novalloy-S S7900 (Type G) | Daicel Polymer Ltd. | PC+ABS | Novalloy-S |
| DENILUB Y 30G 3TF | Vamp Tech | Nylon 66 | DENILUB |
| ICORENE® 3979 | ICO Polymers APAC, A Division of A. Schulman | mHDPE | ICORENE® |