Electrafil® J-1200/CF/20
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h8Z1lN_Electrafil-J-1200-CF-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil®J-1200/CF/20 is an acrylonitrile butadiene styrene (ABS) product, which contains a filler of 20% carbon fiber reinforcement. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Electrafil®The application fields of J-1200/CF/20 include packaging, engineering/industrial accessories, automobile industry, commercial/office supplies and conveyor belts. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.050 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 13800 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 96.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 1.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 12400 | MPa | ASTM D790 |
| Flexural Strength (Break, 23°C) | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.18 mm) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 104 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 102 | °C | ASTM D648 |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 50 | ohms | ASTM D257 |
| Volume Resistivity | 5.0 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Surface Resistivity, ASTM D257: 10-100 ohms/sqVolume Resistivity, ASTM C611: 1-10 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 - 87.8 | °C | |
| Drying Time | 2.0 - 16 | hr | |
| Rear Temperature | 216 - 232 | °C | |
| Middle Temperature | 221 - 238 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 199 - 221 | °C | |
| Processing (Melt) Temp | 232 - 260 | °C | |
| Mold Temperature | 71.1 - 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ARMAMID® PA TM 15.1 | Poly Plastic | Nylon 6 | ARMAMID® |
| Clariant Nylon 6 PA213M40 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| HOPELEN H1500 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |
| Karina WHITE PVC COMPOUND -E 839-10/ 68-Y-CRA | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Evoprene™ GC 082 | Mexichem Specialty Compounds Inc. | TPE | Evoprene™ GC |