Zytel® HTN 53G50HSLR NC010
| Category: | Nylon, Unspecified , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h8NcXp_Zytel-HTN-53G50HSLR-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% Glass Reinforced High Performance Polyamide with Improved Impact and Stiffness |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.59 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.40 | -- | % | |
| Flow | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16500 | 16300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 250 | 215 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.8 | 3.1 | % | ISO 527-2 |
| Flexural Modulus | 15000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 14 | -- | kJ/m² | |
| 23°C | 15 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 95 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 14 | -- | kJ/m² | |
| 23°C | 15 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 236 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.4E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 1.7E-5 | -- | cm/cm/°C | |
| Transverse | 5.5E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 5.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 25 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 27 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M3700C (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| RTP 1085 TFE 15 | RTP Company | PBT | RTP |
| Ghaed ABS ABS-65 | Ghaed Basir Petrochemicals Co. | ABS | Ghaed ABS |
| LUVOCOM® G | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Polygen SG8A-BK | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |