Next Nylon 6 Industrial Series NGIM15-02BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Industrial Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h8MXYp_Next-Nylon-6-Industrial-Series-NGIM15-02BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Glass Fiber Reinforced Impact modified Black Compound Product Applications It is generally recommended for application such as window hardware, Wheel chairs wheel, Bicycle wheel, Power tool housing, hose clamps etc Benefits Good Toughness in combination with a balance strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.22 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.40 | -- | % | |
| Across Flow | 1.1 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.1 | -- | % | |
| Saturation 1 | 6.2 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 110 | -- | ||
| R-Scale | 120 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 90.0 | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | 15 | % | ASTM D638 |
| Flexural Modulus | 5400 | 2600 | MPa | ASTM D790 |
| Flexural Strength | 155 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 88 | 150 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 205 | -- | °C | |
| 1.8 MPa, Unannealed | 185 | -- | °C | |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | 20 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROPRENE® 1 A50 M1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| Badamid® LB70 K | Bada AG | Nylon 6 | Badamid® |
| Geon™ Vinyl Rigid Extrusion 87262 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| OmniPro™ HPP GRC30 | OMNI Plastics, LLC | PP Homopolymer | OmniPro™ |
| LEXAN™ EXL1414T resin | SABIC Innovative Plastics | PC | LEXAN™ |