Hifax 5519/1 G 1750
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h85lnr_Hifax55191G1750.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hifax 5519/1 G 1750 is a less then 10% talc filled PP copolymer, with good impact resistance. Product is available as a customized color matched, pellet form. This grade is delivered in 1750 color version. This grade is not intended for medical, pharmaceutical, food and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.970 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 17.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 100 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 1250 | MPa | ISO 178/A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.2 | kJ/m² | ISO 179/1eA |
| 23°C | 60 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 47.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotec® ASA E 210 | ROMIRA GmbH | ASA | Rotec® ASA |
| KPOL-HDPE HD K-I 2/949 | KPOL Chem Co. | HDPE | KPOL-HDPE |
| Kafrit PEX TA 2125 HD | Kafrit NA Ltd. | XLPE | Kafrit PEX |
| SIBUR Synthetic Rubber NBR 2675 | SIBUR | NBR | SIBUR Synthetic Rubber |
| Moplen HP552R | LyondellBasell Industries | PP Homopolymer | Moplen |