MAJORIS FC187C - 9444
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h7bEB2_MAJORIS-FC187C---9444.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FC187C - 9444 is a mineral filled high performance compound intended for injection moulding. FC187C - 9444 is intended for component, which require very good surface quality, rigidity, low shrinkage and high dimensional stability. The product is UV stabilised. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2250 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 30.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 2000 | MPa | ISO 178 |
| Flexural Stress | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.2 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 54 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 111 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 71.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Fluorosint® HPV | Quadrant Engineering Plastic Products | PTFE | Quadrant EPP |
| Staramide RF004EU | Eurostar Engineering Plastics | Nylon 66/6 | Staramide |
| Badamid® LB70 GF M45 FR HF | Bada AG | Nylon 6 | Badamid® |
| Fainplast PVC GK 88/3 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LUVOCOM® 6/CF/30 | Lehmann & Voss & Co. | Nylon 12 | LUVOCOM® |