Menzolit® SMC 2400
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h7QOr8_Menzolit-SMC-2400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® SMC 2400 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® SMC 2400 is a SMC with extraordinary fire retardancy. The glass level has been selected to combine mouldability with strength and stiffness properties. The fire retardancy is especially high, and the material is virtually nonburnable. In case of fire smoke is released to a small extent. Smoke is, except for carbon monoxyde non-toxic! This makes SMC 2400 very suitable for railway interior or exterior applications, like wall panels, window frames, lugage bins, seat shells and structures or similar rail way components. Fire safe furniture or sanitary furniture on ships, trains or prison cells are another typical use. Within the electrical industry it is used for arc quenching chambers or switch gear components that are exposed to high power switching operations and resulting electrical arcs (peak loads of temperature and fire). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.90 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.080 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 9000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 58.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 9000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 70 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 165 | °C | Internal Method |
| Glass Transition Temperature | 170 | °C | DSC |
| CLTE - Flow | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 70 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Glow Bar | Level BH 2 <= 10 | IEC 60707-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 150 | °C | |
| Injection Pressure | 8.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell Polyamide CR-16 | Adell Plastics, Inc. | Nylon, Unspecified | Adell Polyamide |
| Chemraz 640 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Delrin® FG900P NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| EPT 4095 | Mitsui Chemicals, Inc. | EPDM | EPT |
| Elvakon® 4453 | Lucite International Holland BV | Acrylic (PMMA) | Elvakon® |