LNP™ THERMOCOMP™ 9X06482 compound
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h7CCop_LNP-THERMOCOMP-9X06482-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* 9X06482 is a compound based on Nylon 4/6 resin containing 30% Glass Fiber. Added feaure of this grade is: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound STN-F-1006 HS Product reorder name: 9X06482 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.58 | % | |
| Across Flow : 24 hr | 1.8 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 1.5 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9540 | MPa | ASTM D638 |
| -- | 9210 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 169 | MPa | ASTM D638 |
| Break 3 | 168 | MPa | ASTM D638 |
| Break | 165 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 4 | 3.5 | % | ASTM D638 |
| Break | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 8240 | MPa | ASTM D790 |
| -- 6 | 7930 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 253 | MPa | ISO 178 |
| Break, 50.0 mm Span 7 | 256 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 71 | J/m | ASTM D256 |
| 23°C 8 | 8.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 860 | J/m | ASTM D4812 |
| 23°C 9 | 51 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.50 | J | ASTM D3763 |
| -- | 2.40 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 289 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 290 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 286 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 286 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.7E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymer-E V26061 | Asia Polymer Corporation (APC) | EVA | Polymer-E |
| Desmovit® DP R CF30 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| Elastron® G P.G401.A60.N | Elastron USA, Inc. | SEBS | Elastron® G |
| NHU-PPS 21330C/F | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |
| 3M™ Dyneon™ Perfluoroelastomer PFE 7301BZ | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |