Staramide BG3H
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h70MqE_Staramide-BG3H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide BG3H is a Heat Stabilized, 15 % Glass Fiber Reinforced Polyamide 6 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.45 to 0.85 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 8.0 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 125 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 4750 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 3(23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength 4(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5 | ISO 180/1U | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 212 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 190 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 206 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 5.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.0E-4 | cm/cm/°C | |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 7 | > 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (3.20 mm, in Oil) | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.60 | ||
| 60 Hz | 3.60 | ||
| 1 MHz | 3.40 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 6.1E-3 | ||
| 60 Hz | 6.1E-3 | ||
| 1 MHz | 0.016 | ||
| Comparative Tracking Index | IEC 60112 | ||
| -- | 550 | V | |
| Solution B | 450 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 3.00 mm | HB | ||
| Oxygen Index | 24 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 82.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 120*10*4 |
| 7 . | ROA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2107 Z | RTP Company | PEI | RTP |
| SABIC® LDPE HP2027N | SABIC Americas, Inc. | LDPE | SABIC® LDPE |
| VESTOLIT® B 7021 Ultra | VESTOLIT GmbH & Co. KG | PVC Homopolymer | VESTOLIT® |
| OMIKRON TMT 51 NERO | TECNOPOL | PP Copolymer | OMIKRON |
| Hostacom HKC 182L C11504 | LyondellBasell Industries | PP Homopolymer | Hostacom |