LNP™ STAT-KON™ FD000 compound
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h6m4lz_LNP-STAT-KON-FD000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON FD000 is an unfilled Polyethylene. Added feature of this grade is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound F- Product reorder name: FD000 |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.04 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 2.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2220 | MPa | ASTM D638 |
| -- | 1400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 33.0 | MPa | ASTM D638 |
| Yield | 32.0 | MPa | ISO 527-2/5 |
| Break 3 | 32.0 | MPa | ASTM D638 |
| Break | 31.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 6.1 | % | ASTM D638 |
| Yield | 5.6 | % | ISO 527-2/5 |
| Break 5 | 9.0 | % | ASTM D638 |
| Break | 6.6 | % | ISO 527-2/5 |
| Flexural Modulus 6(50.0 mm Span) | 1300 | MPa | ASTM D790 |
| Flexural Stress | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 19 | J/m | ASTM D256 |
| 23°C 7 | 2.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 890 | J/m | ASTM D4812 |
| 23°C 8 | 53 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.4 | J | ASTM D3763 |
| -- | 14.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 90.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 84.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 51.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 51.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0 to 3.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viton® A-201C | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| Bexloy® W | DuPont Packaging & Industrial Polymers | Ionomer | Bexloy® |
| CABELEC® CC6057 | Cabot Corporation | PP Copolymer | CABELEC® |
| Karina LIGHT BLUE PVC COMP. -E600D06/958 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pinnacle PP 5155C3 | Pinnacle Polymers | PP Random Copolymer | Pinnacle PP |