Latamid 12 H2 K/30
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h6eiHC_Latamid-12-H2-K-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 12 (PA 12). Heat stabilised. Carbon fibre. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.60 to 0.90 | % | |
| Flow : 2.00 mm | 0.20 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 16000 | MPa | |
| 60°C | 7200 | MPa | |
| 90°C | 6600 | MPa | |
| 120°C | 3900 | MPa | |
| 150°C | 2600 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 140 | MPa | |
| Break, 60°C | 95.0 | MPa | |
| Break, 90°C | 70.0 | MPa | |
| Break, 120°C | 50.0 | MPa | |
| Break, 150°C | 35.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 3.0 | % | |
| Break, 60°C | 4.5 | % | |
| Break, 90°C | 5.0 | % | |
| Break, 120°C | 6.0 | % | |
| Break, 150°C | 7.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 40 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 70 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 180 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 175 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | °C | |
| Vicat Softening Temperature | 170 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 4.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unipren® Elastomers D3 PRTA011 60A IG06S1 UP345 | Petropol Industry and Trade of Polymers LTDA | TPO (POE) | Unipren® Elastomers |
| Diakon® Frost FR10423 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| LNP™ LUBRILOY™ Lexan_WR6300 compound | SABIC Innovative Plastics | AES+PC+SAN | LNP™ LUBRILOY™ |
| Capilene® CT 71 A | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |
| LEXAN™ EXL1494T resin | SABIC Innovative Plastics | PC | LEXAN™ |