INSULCAST® 3230 LV/INSULCURE 9
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h6F63c_INSULCAST-3230-LV-INSULCURE-9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST 3230 LV is a low viscosity, highly filled epoxy formulation which, in addition to having excellent electrical properties, has unusually high thermal conductivity with low thermal expansion. Similar to INSULCAST 140 but lower viscosity. This system meets the NASA outgassing specifications with tolerances for TML ranging from 0.40 to 0.41% and for CVCM ranging from 0.0 to 0.1%. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Compressive Strength | 114 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 2.8E-5 | cm/cm/°C | |
| Thermal Conductivity | 1.3 | W/m/K | |
| Heat Deflection Temperature | 80 | °C | |
| Service Temperature | 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.3E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 6.30 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.020 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 4.0 to 5.0 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Amber | ||
| -- 2 | Black | ||
| Density | |||
| -- 3 | 0.968 | g/cm³ | |
| -- 4 | 2.09 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| 25°C 5 | 0.055 | Pa·s | |
| -- 6 | 6.0 | Pa·s | |
| 25°C 7 | 18 | Pa·s | |
| Curing Time | |||
| 65°C | 2.0 | hr | |
| 25°C | 16 to 24 | hr | |
| Pot Life 8(25°C) | 75 to 120 | min |
| Note Message | |
|---|---|
| 1 . | INSULCURE 9 |
| 2 . | INSULCAST 3230 LV |
| 3 . | INSULCURE 9 |
| 4 . | INSULCAST 3230 LV |
| 5 . | INSULCURE 9 |
| 6 . | Mixed |
| 7 . | INSULCAST 3230 LV |
| 8 . | 100 gram mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tufel® II 94205 | Momentive Performance Materials Inc. | Silicone | Tufel® II |
| Comai 745-4 AS | Comai Ltda | LLDPE | Comai |
| Flexil™ 22S | Polymer Dynamix | Nylon 12 | Flexil™ |
| Polifor® C L6 GF/30 NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |
| MACOMASS PP MM-PP HE 84 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |