AZDEL™ C467-B01
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Azdel, Inc. |
| Trademark: | AZDEL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h5tSuc_AZDEL-C467-B01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AZDEL C467-B01 is a glass mat thermoplastic laminate based upon random oriented chopped fiber mat and mineral filler contained within polypropylene resin matrix. This composite material features high flow properties and a very homogeneous fiber distribution and exhibits low part warpage after molding. This material is typically used for standard semi-structural thin wall applications and where good glass distribution into features such as ribs and bosses is desired. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5730 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 6210 | MPa | ISO 178 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | ASTM D3763 | ||
| 4.00 mm, Energy at Peak Load | 10.0 | J | ASTM D3763 |
| 4.00 mm, Total Energy | 29.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 160 | °C | ASTM D648 |
| CLTE - Flow (-40 to 121°C) | 3.2E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 0.0 | mm/min | ISO 3795 |
| Additional Information |
|---|
| Basis Weight, Internal Test Method: 1.076 lbs/ft²Filler Content by Weight(ashing), Internal Test Method: 45 %Multi-axial Impact Peak Force, ASTM D3763, 4mm: 579 lbsNotched Izod Impact, ISO 180, 23°C, 4mm: 334 J/mPoissons Ratio, ISO 527: 0.347Sheet Thickness, Internal Test Method: 165 milsSpecific Gravity, ASTM D792, Laminated: 1.28Specific Gravity, ASTM D792, Molded: 1.3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 14N4003 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| RTP 1000.75 FR A | RTP Company | PBT | RTP |
| Clariant Nylon 6/6 PA-131G33 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| FHR EPS 55-5655 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Karina IVORY PVC COMPOUND -E 105900-35/ 1-B-ACE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |