Order Products : sales@su-jiao.com

KPOL-HDPE HD K-I 14/960

Category:	HDPE , High Density Polyethylene
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-HDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	h5PTEC_KPOL-HDPE-HD-K-I-14-960.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High Density Polyethylene HDPE Homopolymer

Characteristics

This resin has a good melt flow with high rigidity and hardness. Its narrow molar mass distribution results in a low tendency to warpage.

Applications

KPOL® HD K-I 14/960 is a high-density polyethylene, developed for the injection molding, easy to process and with high productivity. Applications : Caps, crates for industrial, transportation or fishing uses, buckets, stands and pallets, trash containers, bottle cases, safety helmets, cages for poultry transportation, sporting goods and Housewares, toys and general purpose containers for indoor applications.

General Information
Additive	Antioxidant (300 to 600 ppm) UV Stabilizer
Features	Antioxidant Good Flow Good Processability Good UV Resistance High Density High Hardness High Rigidity Homopolymer Low Warpage Narrow Molecular Weight Distribution
Uses	Caps Containers Crates Household Goods Safety Helmets Sporting Goods Toys
Agency Ratings	FDA 21 CFR 177.1520
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.960	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	14	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	58		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	27.0	MPa	ASTM D638
Tensile Elongation ²(Break)	12	%	ASTM D638
Flexural Modulus - 1% Secant	1250	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	33	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	78.0	°C	ASTM D648
Vicat Softening Temperature	127	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
RANPELEN SFI-841	Lotte Chemical Corporation	PP Terpolymer	RANPELEN
TEKAMID™ H14HR	Mando Advanced Materials Co., Ltd.	ABS+Nylon	TEKAMID™
KRATON® D1192 A	Kraton Polymers LLC	SBS	KRATON®
INELEC PA612CF30	Infinity LTL Engineered Compounds	Nylon 6/12	INELEC
LEXAN™ HPX8R resin	SABIC Innovative Plastics	PC	LEXAN™