Infino NH-1017D
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h5547V_Infino-NH-1017D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino NH-1017D is a Polycarbonate + ABS (PC+ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 46 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 59.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break | 47.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 33 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2400 | MPa | ASTM D790 |
| -- 3 | 2500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 83.0 | MPa | ASTM D790 |
| -- 5 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 15 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 590 | J/m | ASTM D256 |
| 23°C 7 | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 93.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 98.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 4.00 mm | 82.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 91.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ISO 306/B50 |
| -- | 100 | °C | ISO 306/B120 |
| RTI Elec (2.00 mm) | 85.0 | °C | UL 746 |
| RTI Imp (2.00 mm) | 85.0 | °C | UL 746 |
| RTI Str (2.00 mm) | 85.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 2.00 mm | V-0 5VB | ||
| 3.00 mm | V-0 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE TPE EE-2275B-01 BLACK | Teknor Apex Company | TPE | Sarlink® TPE |
| AIE PPO 9010F-S085A | Asia International Enterprise (Hong Kong) Limited | PPE+PS | AIE PPO |
| Fiberfil® PP-60/FR | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Globalprene® 3545 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| INSPIRE™ 137 (Film Extrusion) | Braskem Europe GmbH | PP, Unspecified | INSPIRE™ |