Rilsamid® AMNO TLD
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Arkema |
| Trademark: | Rilsamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h51xkG_Rilsamid-AMNO-TLD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsamid ® AMNO TLD is a natural polyamide 12. This grade is designed for injection molding. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/2.16 kg) | 57.0 | cm³/10min | ISO 11357 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 30°C, 24 hr, 2.00 mm | 0.80 | % | |
| Flow : 30°C, 24 hr, 2.00 mm | 0.80 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1230 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 38.0 | MPa | |
| Break | 64.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 7.0 | % | |
| Break | > 200 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 178 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | V-2 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA12, MHLR, 12-010 | ISO 1874 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 230 to 290 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PVC Film 588 | Teknor Apex Company | PVC, Flexible | PVC Film |
| Sylvin 6185-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Karina BLACK PVC COMPOUND 970-DA-48/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RC003SXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ THERMOCOMP™ |
| Plasmer 1090N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |