Hanwha Total PP FB52
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h4n2vD_Hanwha-Total-PP-FB52.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FB52 uses base resins with superior impact resistance, resulting in exceptionally high impact strength. In particular, FB52 features superior flowability offering excellent processability, high flame retardancy. This compound PP is widely used in electric and electronic component housings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.1 - 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 88 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 28.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 30 | % | ASTM D638 |
| Flexural Modulus 3 | 1570 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 115 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.794 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 180 - 200 | °C | |
| Nozzle Temperature | 190 - 210 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Injection Pressure | 39.2 - 78.5 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa |
| Injection instructions |
|---|
| Injection Speed: 50 to 80 % |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRILAC® ABS-HH2000 | Polymer Technology and Services, LLC | ABS | TRILAC® |
| Ferro PP LPP40BK69HB-BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Globalene® 73F4-4 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| Delene 1150 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |
| ULTEM™ 2100F resin | SABIC Innovative Plastics Europe | PEI | ULTEM™ |