DIALAC® S210B
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | UMG ABS, Ltd. |
| Trademark: | DIALAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h4aLL7_DIALAC-S210B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DIALAC® S210B is an Acrylonitrile Styrene Acrylate (ASA) material. It is available in Asia Pacific or North America for injection molding. Primary attribute of DIALAC® S210B: RoHS Compliant. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.40 to 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 108 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2350 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 47.0 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 73.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 2.0 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 83.0 | °C | ISO 75-2/Af |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 220 to 250 | °C | |
| Nozzle Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C | |
| Injection Pressure | 70.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 5.00 to 15.0 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LDF 700-B | Marco Polo International, Inc. | LDPE | MARPOL® |
| Abstron HI-40 | Bhansali Engineering Polymers Limited | ABS | Abstron |
| ALTECH® POM A 3030/500 GB30 | ALBIS PLASTIC GmbH | Acetal (POM) Copolymer | ALTECH® POM |
| LEXAN™ HFD1034 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| TECHNYL STAR® S 218L1 V30 BLACK 1N | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |