Crastin® SK602 NC010
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h4PtBP_Crastin-SK602-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% Glass Reinforced Polybutylene Terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 | % | |
| Flow | 0.40 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.42 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.17 | % | |
| Viscosity Number | 105 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 109 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 5300 | MPa | |
| 1000 hr | 4300 | MPa | |
| Flexural Modulus | 5200 | MPa | ISO 178 |
| Flexural Stress | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 7.0 | kJ/m² | |
| -30°C | 7.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C | 40 | kJ/m² | |
| -30°C | 45 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 6.0 | kJ/m² | |
| -30°C | 6.0 | kJ/m² | |
| 23°C | 6.5 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -40°C | 30 | kJ/m² | |
| -30°C | 50 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 55.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 5.0E-5 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 27 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.10 | ||
| 1 MHz | 3.50 | ||
| Dissipation Factor | |||
| 1 kHz | 8.0E-3 | ASTM D150 | |
| 1 MHz | 0.020 | ASTM D150, IEC 60250 | |
| 100 Hz | 2.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | 30 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB | ||
| Oxygen Index | 19 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.22 | g/cm³ | |
| Specific Heat Capacity of Melt | 1900 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.24 | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom RJ72470 | Spartech Polycom | PVC Alloy | Spartech |
| TIPOLEN® FD 243-51 | MOL Petrochemicals Co. Ltd. | LDPE | TIPOLEN® |
| Next Nylon 6 Industrial Series NG15-02JBK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Industrial Series |
| APEX® 3202-80NT | Teknor Apex Company | PVC, Flexible | APEX® |
| KPOL-PP K-PPC 20.0 | KPOL Chem Co. | PP Impact Copolymer | KPOL-PP |