HiFill® PEEK CF30 A NAT
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h4PQMg_HiFill-PEEK-CF30-A-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PEEK CF30 A NAT is a Polyetheretherketone (PEEK) product filled with carbon fiber. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 262 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.7 | % | ASTM D638 |
| Flexural Modulus | 22800 | MPa | ASTM D790 |
| Flexural Strength | 379 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 335 | °C | ASTM D648 |
| CLTE - Flow | 1.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+3 | ohms·cm | ASTM D257 |
| Shielding Effectiveness - 30 to 1000 MHz | 30 | dB | ASTM D4935 |
| Static Decay | < 0.500 | FTMS 101B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 249 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 360 to 388 | °C | |
| Middle Temperature | 360 to 388 | °C | |
| Front Temperature | 360 to 388 | °C | |
| Processing (Melt) Temp | 360 to 382 | °C | |
| Mold Temperature | 177 to 218 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Novalloy-A A2602 | Daicel Polymer Ltd. | ABS+Nylon | Novalloy-A |
| DIOSHY® HG-795-10-4 | DIOSHY Co.,Ltd. | SEBS | DIOSHY® |
| Geon™ Vinyl Packaging XPL 293 FROST 1733 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Packaging |
| Hylac® GP74G20 | Ravago Manufacturing Americas, LLC | ABS | Hylac® |
| SQUARE® LIM1962-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |