VALOX™ 735 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h3E6Ir_VALOX735resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/natural only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Specific Volume | 0.621 | cm³/g | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.40 - 0.60 | % | Internal method |
| Flow 2 | 0.30 - 0.40 | % | Internal method |
| Transverse flow 3 | 0.40 - 0.60 | % | Internal method |
| Transverse flow 4 | 0.60 - 0.80 | % | Internal method |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 5(Break) | 75.8 | MPa | ASTM D638 |
| Flexural Modulus 6(50.0 mm Span) | 8270 | MPa | ASTM D790 |
| Flexural Strength 7(Break, 50.0 mm Span) | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 430 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 216 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 199 | °C | ASTM D648 |
| CLTE - Flow | ASTM E831 | ||
| -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| 60 to 138°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.3E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Oil | 30 | kV/mm | ASTM D149 |
| 3.20 mm, in Air | 24 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 4.30 | ASTM D150 | |
| 1 MHz | 4.00 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 0.020 | ASTM D150 | |
| Arc Resistance 8 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.813 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 243 - 254 | °C | |
| Middle Temperature | 249 - 260 | °C | |
| Front Temperature | 254 - 266 | °C | |
| Nozzle Temperature | 254 - 271 | °C | |
| Processing (Melt) Temp | 254 - 277 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.025 - 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 3.2 to 4.6 mm |
| 2 . | 1.5 to 3.2 mm |
| 3 . | 1.5 to 3.2 mm |
| 4 . | 3.2-4.6 mm |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F280 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Elastollan® 1085 A | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| HiFill® PA6/6 GF33 IM HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Jiangsu Sinarise JM8713-1 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| POLYFLON™ M-18 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |