PALPROP® R H 15 GF 20

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	pal plast GmbH
Trademark:	PALPROP®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	h1SyzH_PALPROP-R-H-15-GF-20.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PALPROP®R H 15 GF 20 is a polypropylene homopolymer (PP Homopoly) product, and the filler is 20% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. PALPROP®R H 15 GF 20 applications include the housing and automotive industries. Features include: Homopolymer anti-warping Good stiffness Impact resistance

General Information
Filler / Reinforcement	Glass fiber reinforced material, 20% filler by weight
Features	Low warpage Rigid, good Homopolymer Impact resistance, good
Uses	Application in Automobile Field Shell
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.05	g/cm³	ISO 1183
Water Absorption (Saturation, 23°C)	1.9	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	4250	MPa	ISO 527-2/1A/1
Tensile Stress (Break, 23°C)	72.5	MPa	ISO 527-2/1A/5
Tensile Strain (Break, 23°C)	4.0	%	ISO 527-2/1A/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	7.5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	38	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	123	°C	ISO 306/B50
Melting Temperature (DSC)	165	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 4000 to 4500 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 70 to 75 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 3 to 5 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 35 to 40 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 6 to 9 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 120 to 125 °CDensity, ISO 1183: 1.04 to 1.06 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 1.8 to 2 %

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 4000 to 4500 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 70 to 75 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 3 to 5 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 35 to 40 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 6 to 9 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 120 to 125 °CDensity, ISO 1183: 1.04 to 1.06 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 1.8 to 2 %

Resin Grade	Manufacturer	Category	Trademark
Santoprene™ 251-92W232	ExxonMobil Chemical	TPV	Santoprene™
NOVALAC FM 4004F	Vyncolit N.V.	Phenolic	NOVALAC
Glastic® UTR	Glastic Corporation	Polyester, TS	Glastic®
Lotrène® LDPE FD0374	QAPCO	LDPE	Lotrène® LDPE
Hifax TYC 356P G14008	LyondellBasell Industries	PP Copolymer	Hifax