Vydyne® 66B
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h1MUnH_Vydyne-66B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vydyne 66B is a high-viscosity PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66B resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils. Typical Applications/End Uses: Typical uses include packaging films, monofilaments, bristles, rods, tubing, sheet and extruded profiles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 2.00mm | 2.0 | -- | % | ISO 294-4 |
| Flow direction : 2.00mm | 2.1 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 8.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | 1800 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield, 23°C | 85.0 | 55.0 | MPa | ISO 527-2/1A |
| Fracture, 23°C | 55.0 | 70.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Yield, 23°C) | 5.0 | 20 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | > 25 | > 150 | % | ISO 527-2/1A |
| Flexural Modulus (23°C) | 3100 | 900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 90.0 | 30.0 | MPa | ISO 178 |
| Poisson's Ratio (23°C) | 0.42 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | 23 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180 | |||
| -30°C | 6.0 | 6.0 | kJ/m² | ISO 180 |
| 23°C | 6.0 | 25 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 195 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00mm | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C, 2.00mm | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec | UL 746 | |||
| 0.710 mm | 130 | -- | °C | UL 746 |
| 1.50 mm | 130 | -- | °C | UL 746 |
| 3.00 mm | 130 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 0.710 mm | 75.0 | -- | °C | UL 746 |
| 1.50 mm | 75.0 | -- | °C | UL 746 |
| 3.00 mm | 75.0 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 0.710 mm | 85.0 | -- | °C | UL 746 |
| 1.50 mm | 85.0 | -- | °C | UL 746 |
| 3.00 mm | 85.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (1.00 mm) | 26 | -- | kV/mm | IEC 60243 |
| Arc Resistance (3.00 mm) | PLC 5 | -- | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.710 mm | PLC 0 | -- | UL 746 | |
| 1.50 mm | PLC 0 | -- | UL 746 | |
| 3.00 mm | PLC 0 | -- | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.710 mm | PLC 4 | -- | UL 746 | |
| 1.50 mm | PLC 3 | -- | UL 746 | |
| 3.00 mm | PLC 2 | -- | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.710 mm | HB | -- | UL 94 | |
| 1.50 mm | HB | -- | UL 94 | |
| 3.00 mm | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.710 mm | 850 | -- | °C | IEC 60695-2-12 |
| 1.50 mm | 850 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.710 mm | 700 | -- | °C | IEC 60695-2-13 |
| 1.50 mm | 700 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 700 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 28 | -- | % | ASTM D2863 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 250 - 295 | °C | |
| Cylinder Zone 2 Temp. | 250 - 295 | °C | |
| Cylinder Zone 3 Temp. | 250 - 295 | °C | |
| Cylinder Zone 4 Temp. | 250 - 295 | °C | |
| Cylinder Zone 5 Temp. | 250 - 295 | °C | |
| Melt Temperature | 270 - 295 | °C | |
| Die Temperature | 270 - 295 | °C |
| Extrusion instructions |
|---|
| Recommended Extrusion Conditions:Melt Point: 260°CMelt Pressure: 3 to 17 MPaBlow Film Bath Temperature: 20°C to 80°CChill Roll Temperature (Cast Film): 20°C to 80°CScrew Design: General Purpose or Barrier |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 MV HI K1416 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| TUFNYL® SGF 15 RED | SRF Ltd. | Nylon 6 | TUFNYL® |
| NANCAR® 3245C | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| Globalene® PT231 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| NHU-PPS 10200F | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |