RapidVac™ VA-274
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | RapidVac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h1GTnQ_RapidVac-VA-274.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VA-274 is a water clear, rigid polyurethane formulated for room temperature hand-batch or vacuum assisted casting methods. Excellent physical properties can be obtained without the utilization of mercury, MOCA, or TDI. VA-274 is low viscosity to be used in applications with thin wall sections for excellent flow rates. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.05 | g/cm³ | |
| Cured | 1.08 | g/cm³ | |
| Base Resin | 1.16 | g/cm³ | |
| Molding Shrinkage - Flow | 0.50 to 1.0 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2520 | MPa | ASTM D790 |
| Flexural Strength | 115 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 74.0 | °C | |
| 1.8 MPa, Unannealed | 70.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 55 Mix Ratio by Weight: 50 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 240 to 480 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| -- 1 | 0.73 | Pa·s | |
| -- 2 | 0.75 | Pa·s | |
| -- 3 | 0.90 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 15 to 21 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 to 86 | ASTM D2240 | |
| Tensile Strength | 67.6 | MPa | ASTM D638 |
| Tensile Elongation at Break | 7.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 16 hours at 180°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radiflam® A FR 308 NER | Radici Plastics | Nylon 66 | Radiflam® |
| NEFTEKHIM PP 8440G (EPS31HP) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| ADENE LXKA | A.D. Compound spa | PP Homopolymer | ADENE |
| LNP™ LUBRICOMP™ RP004 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| TARFLON™ #2200 | Formosa Idemitsu Petrochemical Corporation | PC | TARFLON™ |