CERTENE™ LLBF-120B
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h1Ewhy_CERTENE-LLBF-120B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLBF-120B is a certified prime resin containing Butene-comonomer, specially designed for production of Blown films for general purpose packaging. LLBF-120B features easy processability with very good film strength as well as wide heat sealing temperature range. LLBF-120B major applications include garment bags, produce bags and liners. Maximum recommended film drawdown is 0.5 mil. LLBF-120B contains no slip and medium antiblock. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 215 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 250 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 12.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 11.0 | MPa | ASTM D882 |
| MD : Break, 25 µm | 45.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 650 | % | ASTM D882 |
| TD : Break, 25 µm | 990 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 85 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 80 | g | ASTM D1922 |
| TD : 25 µm | 550 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm) | 65 | ASTM D2457 | |
| Haze (25.4 µm) | 7.3 | % | ASTM D1003 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® MRGFX1393-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| TRIBIT® 1500G30A30 | Samyang Corporation | PBT | TRIBIT® |
| Colorite Rigid PVC 2600 CLR | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Hifax TRC 280X NA Black | LyondellBasell Industries | PP Copolymer | Hifax |
| LTP LTP8275 | Chengdu Letian Plastics Co., Ltd | PPS | LTP |