ELITE™ 5940ST
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h1329H_ELITE5940ST.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELITE™ 5940ST Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow. It offers a unique combination of excellent stiffness/toughness balance, good tear strength and an outstanding processability, allowing for the production of a variety of downgauged films at high output rates. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.941 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 435 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 432 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 19.4 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 20.3 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 28.2 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 25.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 540 | % | ASTM D882 |
| TD : Fracture, 51 µm | 600 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 280 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm 1 | 120 | g | ASTM D1922 |
| TD : 51 µm 2 | 570 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 123 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 125 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 24 | ASTM D2457 | |
| Haze (50.8 µm) | 30 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 2.5in. (63.5mm); 30:1ratio L/D Screw Type: DSBII Die Gap: 70mil (1.8 mm) Melt Temperature: 442°F (228°C) Output: 7.5 lb/hr/in. of die circumference Die Diameter: 6 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 85.3 rpm Frost Line Height: 30 in. (762mm) |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clariant Nylon 6/6 PA-113G20 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| LONGLITE® PBT 3010-104X | CCP Group | PBT | LONGLITE® PBT |
| REV Materials 8003-002 | REV Materials | PP, Unspecified | REV Materials |
| Petrothene® GA623119 | LyondellBasell Industries | LLDPE | Petrothene® |
| Sylvin 2990-67 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |