Reslen PPH 10/GWT 960 HF
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polimarky Spolka Jawna |
| Trademark: | Reslen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h0rmcK_Reslen-PPH-10-GWT-960-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reslen PPH 10/GWT 960 HF is a Polypropylene Homopolymer (PP Homopolymer) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 to 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 to 20 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 to 1900 | MPa | ISO 527-2 |
| Tensile Stress | 22.0 to 27.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 40 to 100 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.8 to 4.5 | kJ/m² | ISO 179/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/A120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santron IMS1000M | Bhansali Engineering Polymers Limited | SAN | Santron |
| Algoflon® S 121 | Solvay Specialty Polymers | PTFE | Algoflon® |
| INEOS PP 500-NA01 | INEOS Olefins & Polymers Europe | PP Impact Copolymer | INEOS PP |
| MAJORIS G410 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| OTECH PVC PF5513-Sandal | OTECH Corporation | PVC, Unspecified | OTECH PVC |