SLOVALEN® PC 93 T 20
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Plastcom |
| Trademark: | SLOVALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h0Xwre_SLOVALEN-PC-93-T-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified PP for injection moulding with the content of 20 % mineral filling, uv stabilized. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. General application in all industry branches. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 2.4 | % | |
| Flow | 2.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2050 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 22.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 30 | % | ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Flexural Stress | 33.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 40 | kJ/m² | |
| 23°C | 90 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 125 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 200 to 250 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® FP25S | BASF Leuna GmbH | Nylon 6 | Miramid® |
| SUSTADUR PBT | Röchling Sustaplast SE & Co. KG | PBT | SUSTADUR |
| TAROMID B 280 G3 K3 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| CP PRYME® Polycarbonate PC100RUL-10M Clear | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Sylvin 4215-80 Grey 9597 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |