Centrene® HDF193B
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Centrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h0VVBD_Centrene-HDF193B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Centrene® HDF193B is a black high molecular weight bimodal PE100 High Density Polyethylene. It is a high performance resin for use in pressure pipes where service life to 100 years is required. HDF193B offers a balance of excellent processing characteristics along with outstanding toughness, chemical resistance and slow crack growth resistance . HDF193B will also provide excellent resistance to the effects of ultra-violet light exposure in outdoor applications due to well dispersed carbon black. Centrene® HDF193B is suitable for extrusion into a full range of pipes, where High Density, PE 100 type resins are required. In particular, a broad processing window and good sag resistance enables the extrusion of larger bore, thick wall pipe. HDF193B is suitable for use in the transport of a wide range of fluids for industrial, rural and mining applications, including potable water. Suitability for use in any application should be determined by appropriate performance testing. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 8.9 | g/10 min | |
| 190°C/5.0 kg | 0.30 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(1.90 mm) | 1300 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 1.90 mm | 26.0 | MPa | |
| Break, 1.90 mm | 33.0 | MPa | |
| Tensile Elongation 3(Break, 1.90 mm) | 760 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 4 | 1150 | MPa | ASTM D790 |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 883 TFE 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| Bergamid™ B700 G15 H NC052 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Elastollan® 1154D | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| ELASTOSIL® R plus 4305/65 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Durethan® BKV 115 DUS008 000000 | LANXESS Corporation | Nylon 6 | Durethan® |