Ingeo™ 6202D
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | h06XzI_Ingeo-6202D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NatureWorks® PLA polymer 6202D, a NatureWorks LLC product, is a thermoplastic fiber-grade resin derived primarily from annually renewable resources. Available in pellet form, 6202D is designed for extrusion into mechanically drawn staple fibers using conventional fiber spinning and drawing equipment. NatureWorks® PLA 6202D can be converted into a broad range of fiber products and is recommended for non-dyed fiber applications. Potential applications for PLA polymer 6202D include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 15 to 30 | g/10 min | ASTM D1238 |
| Relative Viscosity | 3.10 | Internal Method | |
| Shrinkage - Hot Air 1(130°C) | < 8.0 | % | ASTM D2102 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Modulus of Elasticity | 30.0 to 40.0 | g/denier | ASTM D2256 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Denier - per filament | > 0.500 | ||
| Elongation of Fibers | 10 to 70 | % | ASTM D2256 |
| Tenacity of Fibers | 2.50 to 5.00 | g/denier | ASTM D2256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 55.0 to 60.0 | °C | ASTM D3417 |
| Peak Crystallization Temperature (DSC) | 155 to 170 | °C | ASTM D3418 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density (230°C) | 1.08 | g/cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 5.0E-3 | % | |
| Melt Temperature | 220 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | 10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL STAR™ SX 218 V50 BLACK 38N-K | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| DOW™ LDPE 525E | The Dow Chemical Company | LDPE | DOW™ LDPE |
| UPES® 315-FLR | NOVA Chemicals | PS+PE | UPES® |
| Nypol® PA A3 G35 HS UV RH PRTA010 NR346 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| LNP™ COLORCOMP™ 241RC compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |