Kingfa API-4008
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gzbB0G_Kingfa-API-4008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa API-4008 is a polypropylene material, which contains a 40% filler. This product is available in North America or Asia Pacific,. The main features of Kingfa API-4008 are:
The typical application field of Kingfa API-4008 is: automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.90 - 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, Injection Molded) | 38.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, Injection Molded) | 10 | % | ASTM D638 |
| Flexural Modulus 3(23°C, Injection Molded) | 3500 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, Injection Molded) | 44.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20mm, injection molding | 25 | J/m | ASTM D256 |
| 23°C, 3.20mm, injection molding | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm, injection molding | 130 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm, injection molding | 70.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| Filler Content, ISO3451/1, Method A: 40% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAMID 66 GF 30 | Röchling Sustaplast SE & Co. KG | Nylon 66 | SUSTAMID |
| DeWAL DW 400 | DeWAL Industries | UHMWPE | DeWAL |
| G-Lene E36A060 | Gas Authority of India Limited | LLDPE | G-Lene |
| POTICON KT16 | Otsuka Chemical Co., Ltd. | PEEK | POTICON |
| Sylvin 8784-77 White 1360 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |