Lion Idemitsu Composites PPS C-719SG
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | Lion Idemitsu Composites PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gzVxGK_Lion-Idemitsu-Composites-PPS-C-719SG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lion Idemitsu Composites PPS C-719SG is a Polyphenylene Sulfide (PPS) product filled with 50% carbon\mineral. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.99 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.70 | % | |
| Flow | 0.30 | % | |
| Water Absorption (23°C, 24 hr) | > 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 171 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.1 | % | ISO 527-2 |
| Flexural Modulus | 17400 | MPa | ISO 178 |
| Flexural Stress | 246 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 3.8 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 269 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-5 | cm/cm/°C | |
| Transverse | 4.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+4 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flowability 2(1.00 mm) | 133 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Internal Method |
| 2 . | Thickness 1mm, Cylinder temperature 320°C, Injection pressure 100MPa, Mold temperature 135°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prixene® EL020E20S | POLYMAT | LLDPE | Prixene® |
| ResMart ABS VH-0800 Black | ResMart | ABS | ResMart |
| TECHNO ABS R790P | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| ANYPOL SE-2000P | SH Energy & Chemical | PS (EPS) | ANYPOL |
| InnoTuf® TP-4006 | Innovative Polymers, Inc. | TSU | InnoTuf® |