LNP™ FARADEX™ NS003 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ FARADEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gzOH6K_LNPFARADEXNS003compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Faradex* NS003 is a compound based on PC+ABS Blend resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. Also known as: LNP* FARADEX* Compound PCA-S-1003 Product reorder name: NS003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.24 | g/cm³ | ASTM D792 |
| -- | 1.21 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.35 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.35 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.30 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3110 | MPa | ASTM D638 |
| -- | 2700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 52.4 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2 |
| Fracture | 49.6 | MPa | ASTM D638 |
| Fracture | 46.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.3 | % | ASTM D638 |
| Yield | 3.5 | % | ISO 527-2 |
| Fracture | 4.7 | % | ASTM D638 |
| Fracture | 6.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2990 | MPa | ASTM D790 |
| -- | 2800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 89.6 | MPa | ASTM D790 |
| -- | 86.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 2 | 9.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 570 | J/m | ASTM D4812 |
| 23°C 3 | 32 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 15.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 120 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 115 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 105 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 103 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 5.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 | ohms·cm | ASTM D257 |
| Static Decay 6 | 10 | msec | FTMS 101B |
| Shielding Effectiveness (3.00 mm) | 50 - 65 | dB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 221 - 232 | °C | |
| Middle Temperature | 232 - 243 | °C | |
| Front Temperature | 243 - 254 | °C | |
| Processing (Melt) Temp | 221 - 260 | °C | |
| Mold Temperature | 37.8 - 82.2 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| 6 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 211 | RTP Company | Nylon 66 | RTP |
| Sylvin 9812-70 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Toraycon® 1151W X01 | Toray Resin Company | PBT | Toraycon® |
| Unilex™ UP 8020 | United Polychem | PP Homopolymer | Unilex™ |
| Kingfa JH710 G10D | Kingfa | PC Alloy | Kingfa |