4PET® 9L22130 HL
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | 4Plas |
| Trademark: | 4PET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gzNydS_4PET-9L22130-HL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4PET 9L22130 HL is a Standard Flow 30% Glass Fibre Reinforced Heat Stabilised, Lubricated PET |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Vertical flow direction | 0.90 | % | |
| Flow direction | 0.20 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Moisture Content | < 1000 | ppm | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 150 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -- | 9.0 | kJ/m² | ISO 179 |
| 23°C | 10 | kJ/m² | ISO 179/B |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | ISO 180/1U |
| 23°C | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 215 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 225 | °C | ISO 306/B |
| Melting Temperature 2 | 250 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 30 | kV/mm | IEC 60243-1 |
| Dissipation Factor | IEC 60250 | ||
| 1 Hz | 0.018 | IEC 60250 | |
| 100 Hz | 3.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 90.0 - 140 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 60.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 50 - 70 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Skyrol® SL11 | SKC Inc. | PET | Skyrol® |
| MORETEC™ 0138M | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| EVICOM™ RI5/145 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| KRALASTIC® TE-2200 | Nippon A&L Inc. | ABS | KRALASTIC® |
| ALTECH® PBT + ASA A 2020/510 GF20 | ALBIS PLASTIC GmbH | PBT+ASA | ALTECH® PBT + ASA |