PELPRENE™ P150B-05
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | PELPRENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gyxU14_PELPRENE-P150B-05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PELPRENE™ P150B-05 is a Thermoplastic Polyester Elastomer (TPEE) product. It is available in North America. Typical application: Automotive. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.3 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 65% RH) | 0.36 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A | 98 | JIS K6301 | |
| Shore D | 57 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 38.0 | MPa | |
| 50% Strain | 19.6 | MPa | |
| Tensile Elongation (Break) | 500 | % | ASTM D638 |
| Flexural Modulus | 289 | MPa | ASTM D790 |
| Compressive Strength (10% Strain) | 19.1 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles) | 10.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 176 | kN/m | ASTM D624 |
| Compression Set | 60 | % | JIS K6301 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 117 | °C | ASTM D648 |
| Brittleness Temperature | < -65.0 | °C | JIS K6301 |
| Vicat Softening Temperature | 190 | °C | ASTM D1525 |
| Melting Temperature | 212 | °C | DSC |
| CLTE - Flow | 1.4E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | JIS K2111 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Resilience | 59.0 | JIS K6301 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3880 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Starflex GM1810BA | LyondellBasell Industries | mLLDPE | Starflex |
| BJB Polyurethane TC-277 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Geon™ Vinyl Flexible A65M0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| OmniLon™ PA6 U IM20 BK1000 | OMNI Plastics, LLC | Nylon 6 | OmniLon™ |