MAJORIS ET265 - 1770
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gy3NTI_MAJORIS-ET265---1770.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ET265 - 1770 is a, 20% mineral filled polypropylene compound intended for injection moulding . The product is available in natural ET265 but other colours can be provided on request. ET265 - 1770 has been developed especially for automotive interior parts that requiring excellent scratch resistance, good balance between the impact strength and stiffness and very good surface quality. In addition it has a good UV stability. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 - 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 26.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.0 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 108 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 64.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 78.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8805-95FR BROWN 7153 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Trademark PE mLLD1916F | Trademark Plastics Corporation | mLLDPE | Trademark PE |
| LinGen FR700 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PE, Unspecified | LinGen |
| OTECH PVC OW132 - Wire Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Sylvin 9077-80 Yellow 4161 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |