Sarlink® TPE EE-2290B BLK XRD2 (PRELIMINARY DATA)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gxSO7L_Sarlink-TPE-EE-2290B-BLK-XRD2-PRELIMINARY-DATA-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE EE-2290B BLK XRD2 (PRELIMINARY DATA) is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is: extrusion. Sarlink®The main features of TPE EE-2290B BLK XRD2 (PRELIMINARY DATA) are:
Sarlink®The typical application fields of TPE EE-2290B BLK XRD2 (PRELIMINARY DATA) are: automobile industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shore A, 1 second, injection molding | 92 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 90 | ISO 868 | |
| Shore A, 15 seconds, injection molding | 90 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Transverse flow : 100% strain | 4.30 | MPa | ISO 37 |
| Flow : 100% strain | 6.94 | MPa | ISO 37 |
| Tensile Stress 2 | ISO 37 | ||
| Transverse flow : Fracture | 16.0 | MPa | ISO 37 |
| Flow : Fracture | 9.04 | MPa | ISO 37 |
| Tensile Elongation 3 | ISO 37 | ||
| Transverse flow : Fracture | 830 | % | ISO 37 |
| Flow : Fracture | 480 | % | ISO 37 |
| Tear Strength 4 | ISO 34-1 | ||
| Transverse flow | 60 | kN/m | ISO 34-1 |
| Flow | 59 | kN/m | ISO 34-1 |
| Compression Set 5 | ISO 815 | ||
| 23°C, 22 hr | 34 | % | ISO 815 |
| 70°C, 22 hr | 48 | % | ISO 815 |
| 90°C, 70 hr | 63 | % | ISO 815 |
| 125°C, 70 hr | 87 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | -2.6 | % | ISO 188 |
| Flow : 110°C, 1008 hr | 3.4 | % | ISO 188 |
| Transverse flow : 100% strain 110°C, 1008 hr | 15 | % | ISO 188 |
| Flow : 100% strain 110°C, 1008 hr | 25 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | -7.2 | % | ISO 188 |
| Flow : 125°C, 168 hr | 5.1 | % | ISO 188 |
| Transverse flow : 100% strain 125°C, 168 hr | 17 | % | ISO 188 |
| Flow : 100% strain 125°C, 168 hr | 25 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | -7.0 | % | ISO 188 |
| Flow : 110°C, 1008 hr | -45 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | -2.6 | % | ISO 188 |
| Flow : 125°C, 168 hr | -44 | % | ISO 188 |
| Change in Shore Hardness in Air | ISO 188 | ||
| Support a, 110°C, 1008 hr 8 | -2.6 | ISO 188 | |
| Support a, 110°C, 1008 hr 9 | -3.0 | ISO 188 | |
| Support a, 110°C, 1008 hr 10 | -3.6 | ISO 188 | |
| Support a, 125°C, 168 hr 11 | 0.20 | ISO 188 | |
| Support a, 125°C, 168 hr 12 | 0.0 | ISO 188 | |
| Support a, 125°C, 168 hr 13 | 0.10 | ISO 188 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 292 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 510mm/min |
| 2 . | Type 1, 510mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | B method, right angle specimen (without cut), 510mm/min |
| 5 . | Type a |
| 6 . | Type 1 |
| 7 . | Type 1 |
| 8 . | 15 sec |
| 9 . | 5 sec |
| 10 . | 1 sec |
| 11 . | 15 sec |
| 12 . | 5 sec |
| 13 . | 1 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Qenos PE HD115 | Qenos Pty Ltd | HDPE, HMW | Qenos PE |
| McCann PP M20CHPP10 | McCann Plastics Inc. | PP Homopolymer | McCann PP |
| Cevian®-MAS MAS10, MAS10F | Daicel Polymer Ltd. | MMS | Cevian®-MAS |
| Sylvin 8344-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8280-60 Brown 7433 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |