Tempalux® 30% GF
| Category: | PEI , Polyether Imide |
| Manufacturer: | Westlake Plastics Company |
| Trademark: | Tempalux® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gxF8wn_Tempalux-30-GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
An amorphous thermoplastic polyetherimide, stock shapes from ULTEM® resin possess a combination of useful characteristics, including high strength at elevated temperatures, high modulus, and broad chemical resistance. Tempalux stock shapes are inherently flame resistant with low smoke emission. Tempalux stock shapes display property retention and resistance to environmental stress cracking when exposed to a wide variety of chemicals. The standard color of Tempalux stock shapes is light amber. Glass filled grades appear tan or greenish in color. Tempalux rod, slab, and tubular bar are air annealed for stress relief. Applications Include:
Advantages of Tempalux:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.16 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8960 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 169 | MPa | |
| Break | 159 | MPa | |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 8960 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 228 | MPa | ASTM D790 |
| Compressive Modulus | 6470 | MPa | ASTM D695 |
| Compressive Strength | 212 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 212 | °C | |
| 1.8 MPa, Unannealed | 210 | °C | |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.26 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 1.5E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.406 mm) | V-0 | UL 94 | |
| Oxygen Index | 50 | % | ASTM D2863 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DJSilicone NE-180 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Esmedica V 7142E | Sekisui Chemical Company, Ltd. | PVC, Unspecified | Esmedica V |
| Kotex KG-20MRA | Kotec Corporation | PC | Kotex |
| Karina LILAC PVC COMPOUND 831-34/148-IS RG-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| GELOY™ EXGY0058 resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |