Complet® LCF50-PA66 MT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PlastiComp, Inc. |
| Trademark: | Complet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gx9mRv_Complet-LCF50-PA66-MT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Complet®LCF50-PA66 MT is a polyamide 66 (nylon 66) product, which contains 50% long carbon fiber as filler. It is available in North America, Europe or Asia Pacific. The main features are: Rohs certification. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 37900 | MPa | ASTM D638 |
| Tensile Strength | 283 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 27600 | MPa | ASTM D790 |
| Flexural Strength | 441 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 290 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1200 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 249 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.18 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 282 - 299 | °C | |
| Middle Temperature | 288 - 304 | °C | |
| Front Temperature | 293 - 310 | °C | |
| Nozzle Temperature | 288 - 304 | °C | |
| Processing (Melt) Temp | 293 - 310 | °C | |
| Mold Temperature | 93.3 | °C | |
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 30 - 50 | rpm | |
| Cushion | 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 to 20.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| Injection speed: 2 to 3 in/secInjection pressure: medium to maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200H HS | RTP Company | Nylon 66 | RTP |
| Polymer-E EV103 | Asia Polymer Corporation (APC) | EVA | Polymer-E |
| Next Nylon 6 Prime Series NM40-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Ferro PP NPP00GT22BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| KOPLA PP KPI1022 | KOPLA Co., Ltd. | PP, Unspecified | KOPLA PP |