TOTAL Polypropylene PPC 4170
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gx8ah4_TOTAL-Polypropylene-PPC-4170.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Petrochemicals Polypropylene 4170 is a polypropylene impact copolymer grade with good melt strength for use in the extrusion of blown films. Benefits. 4170 forms tough films with high dart impact strength, high heat resistance and excellent processability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 50 µm, Blown Film | 690 | MPa | |
| 2% Secant, TD : 50 µm, Blown Film | 600 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm, Blown Film | 26.0 | MPa | |
| TD : Yield, 50 µm, Blown Film | 25.0 | MPa | |
| MD : Break, 50 µm, Blown Film | 59.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 38.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 750 | % | |
| TD : Break, 50 µm, Blown Film | 770 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 350 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, Blown Film | 55 | g | |
| TD : 50 µm, Blown Film | 300 | g | |
| Oxygen Transmission Rate (23°C, 0% RH, 50 µm, Blown Film) | 2100 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (38°C, 100% RH, 50 µm, Blown Film) | 7.0 | g/m²/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 160 to 165 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 7 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 72 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 to 250 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALENE® P 100 SGF30 ST F V-0 natural | RIA-Polymers GmbH | PP, Unspecified | RIALENE® |
| Toyolac® TP82-X05 | Toray Resin Company | ABS | Toyolac® |
| NEXUS PE LDPE-1017 | Nexus Resin Group, LLC. | LDPE | NEXUS PE |
| Addisil™ 60 Xray | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| Elastron® G P.G401.A40.N | Elastron USA, Inc. | SEBS | Elastron® G |