Durethan® BTC 65 H3.0 EF 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gwiqFp_DurethanBTC65H30EF901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 65% mineral, injection molding, improved heat conductivity |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 2.01 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.68 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.18 | -- | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 0.66 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.16 | -- | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | 3.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9900 | 3500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 90.0 | 45.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 4.5 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 10200 | -- | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 150 | -- | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.0 | -- | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA6, GHR, 10-090, MD65 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 35 | 25 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 8 | 221 | -- | °C | ISO 11357-3 |
| Thermal Conductivity | ISO 22007-4 | |||
| -- 9 | 1.0 | -- | W/m/K | ISO 22007-4 |
| -- 10 | 1.3 | -- | W/m/K | ISO 22007-4 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Through-plane |
| 10 . | With Flow |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP H7512 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Sylvin 86024-38DUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AMTOPP BA30 | Inteplast Group | PP, Unspecified | AMTOPP |
| Lastane 50 | LATI S.p.A. | PUR, Unspecified | Lastane |
| LG PVC PB900 | LG Chem Ltd. | PVC Homopolymer | LG PVC |