RTP 700 GB 40
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gvX4gS_RTP-700-GB-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Bead |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 to 2.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2070 | MPa | ASTM D638 |
| Tensile Strength | 15.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength | 24.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 530 | J/m | ASTM D4812 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 40 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 193 to 232 | °C | |
| Mold Temperature | 21.1 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1107 | RTP Company | PET | RTP |
| TEKNIFLEX® MED 2001-0200 | Tekni-Films, a div of Tekni-Plex | Film, PP | TEKNIFLEX® MED |
| DynaMix™ 3644-GB | Polymer Dynamix | PPA | DynaMix™ |
| Hostacom CR 1171 G1A | LyondellBasell Industries | PP Impact Copolymer | Hostacom |
| OP - ABS ABS 4-8 SS | Oxford Polymers | ABS | OP - ABS |