| TECHNYL® ALLOY KC 216 V12 Black is a grade based on a blend of polyamide 6 and acrylonitrile butadiene styrene, reinforced with 12% of glass fiber for injection moulding. This grade offers high mechanical properties, good dimensional stability and good processability. It is a synergistic blend material between Polyamide 6 and ABS with an ideal property combination, meaning that it has dual characteristics between semi-crystalline and amorphous polymers. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4800 | 2800 | MPa | ISO 527-2/1A |
| Tensile Stress (Break, 23°C) | 96.0 | 55.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break, 23°C) | 3.3 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4300 | 2700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 160 | 80.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 90 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | 90 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 8.0 | 16 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 40 | 80 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 200 | -- | °C | ISO 75-2/Bf |
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 575 | -- | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 235 - 240 | °C | |
| Middle Temperature | 240 - 250 | °C | |
| Front Temperature | 250 - 260 | °C | |
| Mold Temperature | 70 - 90 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PE 4142L (424F5) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| APEX® 3310-50NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Generic PVDF | Generic | PVDF | Generic |
| Paracril® P3350CC2 | INSA | NBR | Paracril® |
| Hostacom EKC 425N G71412 | LyondellBasell Industries | PP, Unspecified | Hostacom |