DuPont™ Elvax® 3135XZ is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resins. Composition 12 % By Weight Vinyl Acetate comonomer content Thermal Stabilizer: non-BHT antioxidant Applications This resin is designed to provide a low temperature heat seal to itself or many other materials commonly used in flexible packaging applications. The melt properties of this resin allow it to be processed on blown film equipment over a wide range of film thickness and blow-up ratios. It can also be co-extruded with a variety of other polymers. This resin is typically used as low temperature seal layer in co-extruded films.

Message

DuPont™ Elvax® 3135XZ is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resins.

Composition

12 % By Weight Vinyl Acetate comonomer content

Thermal Stabilizer: non-BHT antioxidant

Applications

This resin is designed to provide a low temperature heat seal to itself or many other materials commonly used in flexible packaging applications. The melt properties of this resin allow it to be processed on blown film equipment over a wide range of film thickness and blow-up ratios. It can also be co-extruded with a variety of other polymers. This resin is typically used as low temperature seal layer in co-extruded films.

General Information
Additive	Antioxidant Heat Stabilizer
Features	Antioxidant Copolymer Food Contact Acceptable Good Flexibility Good Heat Seal Heat Stabilized Low Temperature Heat Sealability
Uses	Film Packaging
Agency Ratings	FDA 21 CFR 177.1350(a)(1)
Forms	Pellets
Processing Method	Blown Film Coextruded Film Coextrusion Film Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.930	g/cm³	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.35	g/10 min	ASTM D1238, ISO 1133
Vinyl Acetate Content	12.0	wt%

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	82.0	°C	ASTM D1525, ISO 306
Peak Melting Temperature	95.0	°C	ASTM D3418, ISO 3146
Freezing Point ¹
--	78	°C	ASTM D3418
--	78	°C	ISO 3146

Extrusion	Nominal Value	Unit
Melt Temperature	< 230	°C

Note Message
1 .	DSC

Resin Grade	Manufacturer	Category	Trademark
RTP 4001 TFE 15 SI 2	RTP Company	PPA	RTP
Mylar® J (300 guage)	DuPont Teijin Films U.S.	PET	Mylar®
CP PRYME® Polycarbonate PC100RULUV-18M Black	Chase Plastics Services Inc.	PC	CP PRYME® Polycarbonate
KOPELEN J-330	Lotte Chemical Corporation	PP Impact Copolymer	KOPELEN
Hytrel® 40CB	DuPont Performance Polymers	TPC-ET	Hytrel®