EL-Lene™ H6430BM
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gty7pw_EL-Lene-H6430BM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Lene H6430BM is a high density polyethylene resin suitable for producing beverage bottles by using Extrusion blow molding machine. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.966 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.40 | g/10 min | |
| 190°C/21.6 kg | 30 | g/10 min | |
| Environmental Stress-Cracking Resistance (50°C, 25% Igepal, Compression Molded, F50) | 24.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 29.4 | MPa | |
| Break | 36.3 | MPa | |
| Tensile Elongation 2(Break) | 1200 | % | ASTM D638 |
| Flexural Modulus | 1470 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 250 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Melting Temperature | 132 | °C | ASTM D2117 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1500.5-40D | RTP Company | TPE | RTP |
| Elastron® G G400.A40.N | Elastron USA, Inc. | SEBS | Elastron® G |
| RTP 299 X 141395 | RTP Company | Nylon 66 | RTP |
| Jam HM-5010T2N (EX3) | Jam Petrochemical Company | HDPE | Jam |
| LNP™ LUBRICOMP™ KL002 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |