Durepol® PBT A3 G15 BRC0001 BT322 MSP
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Durepol® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gtidx5_Durepol-PBT-A3-G15-BRC0001-BT322-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT polyester in color white reinforced with 15% of fiberglass, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.060 | % | ASTM D570 |
| Ash Content | 13 to 17 | % | ASTM D2584 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 89.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 160 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4480 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 160 | °C | ASTM D648 |
| Melting Temperature 1 | 224 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefanyl® VE VEEP 115 | Mitsubishi Chemical Performance Polymers, Inc. | PVC+NBR | tefanyl® VE |
| SUMILITE® PVC VSL-4601-N | Sumitomo Bakelite Co., Ltd. | PVDC | SUMILITE® PVC |
| ASI POLYPROPYLENE 1500X-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| MAJORIS AT397 | AD majoris | PP Copolymer | MAJORIS |
| Macromeric® 0103-212b BK | Saco Polymers | Polyolefin, Unspecified | Macromeric® |