EPLAMID 6 IMP V0 NC B001
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLAMID 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gtY2Gg_EPLAMID-6-IMP-V0-NC-B001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flame retardant additived polyamide 6, with improved good-impact resistance, heat stabilized, lubricated for injection molding. Eplamid 6 IMP V0 B001 offers an excellent Notched High Impact resistance with ensures outstanding performance at low temperatures with rating UL94 V0 and glow-wire at 960°C, which is used in many sectors of industy. This material is available in natural and in colours on request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.33 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 1.8 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 1.4 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 78 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4000 | 3850 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 40.0 | 37.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 3.0 | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 3800 | 3650 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 85.0 | 75.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | 14 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 10 | 12 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 250 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | -- | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 750 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riblene® FL 30 | Versalis S.p.A. | LDPE | Riblene® |
| TOLEN H273 FF | SIBUR, LLC | PP Homopolymer | TOLEN |
| TRANSMARE® 10HGF30-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| AvaSpire® AV-481 | Solvay Specialty Polymers | PAEK | AvaSpire® |
| Durethan® BKV 130 GIT DUS008 900116 | LANXESS Corporation | Nylon 6 | Durethan® |