SABIC® PPcompound 8900P
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gtSqoL_SABICPPcompound8900P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 8900P is a mineral filled modified polypropylene. This material combines high flow with a very high stiffness and high impact, as well as a very low shrinkage and CLTE. The high stiffness and low CLTE makes the material suited for high demanding applications. The material is UV stabilized. SABIC® PPcompound 8900P is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.60 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20mm, injection molding | 24.0 | MPa | ISO 527-2/5/50 |
| Fracture, 3.20mm, injection molding | 15.0 | MPa | ISO 527-2/5/50 |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 50 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 2300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/4A | ||
| -20°C, injection molding | 3.5 | kJ/m² | ISO 180/4A |
| 0°C, injection molding | 7.0 | kJ/m² | ISO 180/4A |
| 23°C, injection molding | 30 | kJ/m² | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 130 | °C | ISO 75-2/B |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 4.5E-5 | cm/cm/°C | ASTM D696 |
| 23 to 80°C | 5.5E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP VLF 82209 | RTP Company | PEEK | RTP |
| Geon™ CPVC EC920 | PolyOne Corporation | CPVC | Geon™ CPVC |
| Hostaform® C 2521 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Karina WHITE PVC COMPOUND -E 839-10/ 19-Y-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SQUARE® LIM3919-40A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |